LaCl₃

Density: 3.84 g/cm³

Melting point: 858℃

Purity≥99.99%, water content≤20 ppm, oxygen content≤50 ppm.

Used to prepare  LaCl₃:Ce³⁺ scintillation crystal.

CeCl₃

Density: 3.97 g/cm³

Melting point: 817℃

Purity≥99.99%, water content≤20 ppm, oxygen content≤50 ppm.

Used to prepareLaCl₃:Ce³⁺ scintillation crystal.

LaBr₃

Density: 5.07 g/cm³

Melting point: 788℃

Purity≥99.99%, water content≤20 ppm, oxygen content≤50 ppm.

Used to prepare LaBr₃:Ce³⁺ scintillation crystal.

CeBr₃

Density: 5.18 g/cm³

Melting point: 732℃

Purity≥99.99%, water content≤20 ppm, oxygen content≤50 ppm.

Used to prepareLaBr₃:Ce³⁺ and CeBr₃ scintillation crystal.

CeI₃

Density: 5.68 g/cm³

Melting point: 760℃

Purity≥99.95%, water content≤20 ppm，oxygen content≤200 ppm.

Used to preparecerium-doped LuI₃, GdI₃ and YI₃ scintillation crystal.

EuI₂

Density: 5.50 g/cm³

Melting point: 580℃

Purity≥99.95%, water content≤20 ppm，oxygen content≤300 ppm.

Used to prepareSrI₂:Eu²⁺ scintillation crystal.

GdI₃

Density: 5.23 g/cm³

Melting point: 931℃

Purity≥99.99%, water content≤20 ppm, oxygen content≤50 ppm.

Used to prepareGdI₃:Ce³⁺ scintillation crystal.

LuI₃

Density: 5.64 g/cm³

Melting point: 1,050℃

Purity≥99.99%, water content≤20 ppm, oxygen content≤50 ppm.

Used to prepareLuI₃:Ce³⁺ scintillation crystal.

YI₃

Density: 4.59 g/cm³

Melting point: 997℃

Purity≥99.99%, water content≤20 ppm, oxygen content≤50 ppm.

Used to prepareYI₃:Ce³⁺ scintillation crystal.